ASTM A588 HSLA Steel Powder Grade B

ASTM A588 HSLA Steel Powder Grade B, Thickness 125 to 200 mm (5-8 in.) Product Information -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Powder Grade B, Thickness 125 to 200 mm (5-8 in.) Synonyms -:- For detailed product information, please contact sales. -: -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Powder Grade B characteristics -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Powder Grade B Particle Size -:- For detailed product information, please contact sales. -: -:- -:- 0-15μm ,5-25μm, 15-45μm, 15-53μm,20-63um, 45-75μm, 45-105μm, 45-150μm ,75-150μm. (Various granularities can be customized according to customer requirements) -:- For detailed product information, please contact sales. -:

ASTM A588 HSLA Steel Powder Grade B Applicable processes -:- For detailed product information, please contact sales. -: Laser/electron beam additive manufacturing (SLM/EBM, 3D printing) Direct laser deposition (DLD) Used in thermal spray (TSA) Powder hot isostatic pressing (HIP) Metal injection molding (MIM) Powder metallurgy (PM) Laser cladding (LC), etc. -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Powder Grade B Chemical Composition -:- For detailed product information, please contact sales. -: -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Grade B, Thickness 125 to 200 mm (5-8 in.) Product Information -:- For detailed product information, please contact sales. -: ### **ASTM A588 Grade B: High-Strength Low-Alloy Structural Steel (Thickness 125-200 mm / 5-8 in.)** #### **1. Overview** ASTM A588 Grade B is a **high-strength low-alloy structural steel** in the very thick plate category (125-200 mm / 5-8 inches), specifically engineered for **heavy structural applications** requiring superior atmospheric corrosion resistance. This weathering steel develops a dense, adherent protective oxide patina when exposed to weather, providing approximately **four times the corrosion resistance** of conventional carbon steels. The Grade B composition in this thickness range maintains excellent mechanical properties while offering enhanced durability for massive structural components in demanding applications. #### **2. Chemical Composition** The chemical composition is optimized for heavy section performance and corrosion resistance: | Element | Composition (%) | |---------|-----------------| | Carbon (C) | 0.20 max | | Manganese (Mn) | 0.75 - 1.25 | | Phosphorus (P) | 0.04 max | | Sulfur (S) | 0.05 max | | Silicon (Si) | 0.15 - 0.50 | | Copper (Cu) | 0.20 - 0.40 | | Chromium (Cr) | 0.40 - 0.65 | | Nickel (Ni) | 0.25 - 0.40 | **Heavy Section Composition Features:** - **Enhanced Copper-Chromium System**: Forms superior protective patina in thick sections - **Controlled Carbon Equivalent**: Ensures weldability despite thickness challenges - **Nickel Enhancement**: Improves through-thickness toughness - **Balanced Alloy Ratios**: Optimized for heavy structural applications #### **3. Physical & Mechanical Properties** **Mechanical Properties (for thickness 125-200 mm / 5-8 in.):** | Property | Requirement | |----------|-------------| | **Tensile Strength** | 63 ksi min (435 MPa min) | | **Yield Strength** | 42 ksi min (290 MPa min) | | **Elongation in 2 inches** | 21% min | | **Charpy V-Notch Impact** | 20 ft-lb min at +70°F (21°C) | **Thickness-Dependent Characteristics:** - **Strength Reduction**: Accounted for in structural design calculations - **Maintained Ductility**: Consistent elongation requirements across thickness range - **Through-Thickness Consistency**: Special processing for uniform properties - **Z-Direction Properties**: Enhanced for resistance to lamellar tearing **Physical Properties (Typical):** - **Density**: 0.284 lb/in³ (7,850 kg/m³) - **Modulus of Elasticity**: 29,000 ksi (200 GPa) - **Poisson's Ratio**: 0.29 - **Coefficient of Thermal Expansion**: 6.5 × 10⁻⁶/°F (11.7 × 10⁻⁶/°C) - **Thermal Conductivity**: 41.5 W/m·K at 212°F (100°C) #### **4. Product Applications** Grade B in 125-200 mm thickness is specified for massive structural applications: **Major Bridge Structures:** - Heavy bridge box girders and main beams - Bridge pier caps and foundation elements - Long-span bridge compression members - Major suspension bridge components **High-Rise Construction:** - Super-tall building mega-columns - Heavy transfer trusses and girders - Major structural nodes in skyscrapers - Seismic-resistant structural elements **Heavy Industrial:** - Nuclear facility structural components - Heavy crane support systems - Major industrial plant primary structures - Heavy mining and processing equipment supports #### **5. International Standards & Equivalents** | Region/Country | Standard | Equivalent Grade | Notes | |----------------|----------|------------------|-------| | **International** | **ISO 4952** | E460D | Heavy section weathering steel | | **Europe** | **EN 10025-5** | S355J2W | Weathering steel for thick plates | | **Japan** | **JIS G3125** | SPA-H | High weathering resistance steel | | **China** | **GB/T 4171** | Q355GNH | Weathering steel equivalent | **A588 Grade B Property Progression:** | Thickness Range | Yield Strength min | Tensile Strength min | Reduction Factor | |-----------------|-------------------|---------------------|------------------| | **100-125 mm** | 46 ksi (315 MPa) | 67 ksi (460 MPa) | 8% | | **125-200 mm** | 42 ksi (290 MPa) | 63 ksi (435 MPa) | 16% | | **200-300 mm** | 40 ksi (275 MPa) | 60 ksi (415 MPa) | 20% | #### **6. Fabrication & Quality Assurance** **Advanced Welding Technology:** - **Mandatory Pre-heat**: 300-500°F (150-260°C) based on exact thickness - **Stringent Interpass Control**: Maximum 400°F (205°C) - **Welding Processes**: SAW and FCAW preferred for heavy sections - **Consumables**: High-toughness, low-hydrogen electrodes required **Special Fabrication Requirements:** - **Thermal Cutting**: Pre-heat to 300-400°F (150-200°C) mandatory - **Stress Relieving**: Often specified for complex heavy fabrications - **Non-Destructive Testing**: Extensive UT and RT requirements - **Handling Equipment**: Heavy-duty cranes and supports essential **Enhanced Quality Assurance:** - **Multiple Tension Tests**: From different locations and orientations - **Ultrasonic Examination**: 100% scanning typically required - **Z-Direction Testing**: Mandatory for critical applications - **Strict Chemical Homogeneity**: Comprehensive analysis verification --- **Technical Advantages:** - **Maintained corrosion resistance** in very thick sections - **Significant lifecycle cost savings** through eliminated painting - **High strength-to-weight ratio** for massive structures - **Proven reliability** in international mega-projects **Design and Engineering Considerations:** - **Reduced strength values** must be incorporated in design - **Thermal stress management** critical in thick sections - **Heavy connection design** for optimal load transfer - **Fabrication sequencing** for stress control **Service Performance:** - **Extended patina development** period in thick sections - **Superior performance** in varied atmospheric conditions - **Structural monitoring** recommended for critical applications - **Minimal maintenance** requirements after patina formation **Disclaimer:** This information represents specialized technical data for very thick plate applications. For structural designs using 125-200 mm A588 Grade B steel, consultation with the latest ASTM specification and relevant structural codes is mandatory. All fabrication must be performed by qualified specialists with experience in heavy steel construction, and designs must be approved by professional structural engineers with expertise in heavy section weathering steel applications. -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Grade B, Thickness 125 to 200 mm (5-8 in.) Specification Dimensions Size： Diameter 20-1000 mm Length <4470 mm Size:We can customized as required Standard： Per your request or drawing We can customized as required Properties（Theoretical） Chemical Composition -:- For detailed product information, please contact sales. -: ASTM A588 HSLA Steel Grade B, Thickness 125 to 200 mm (5-8 in.) Properties -:- For detailed product information, please contact sales. -:

ASTM A588 HSLA Steel Powder Grade B Particle Size Description -:- For detailed product information, please contact sales. -: Applications of ASTM A588 HSLA Steel Powder Grade B -:- For detailed product information, please contact sales. -: -:- For detailed product information, please contact sales. -: Applications of ASTM A588 HSLA Steel Powder Grade B, Thickness 125 to 200 mm (5-8 in.) -:- For detailed product information, please contact sales. -: Chemical Identifiers ASTM A588 HSLA Steel Powder Grade B, Thickness 125 to 200 mm (5-8 in.) -:- For detailed product information, please contact sales. -:

Packing of ASTM A588 HSLA Steel Powder Grade B, Thickness 125 to 200 mm (5-8 in.) -:- For detailed product information, please contact sales. -: Standard Packing: -:- For detailed product information, please contact sales. -: Typical bulk packaging includes palletized plastic 5 gallon/25 kg. pails, fiber and Steel Powder drums to 1 ton super sacks in full container (FCL) or truck load (T/L) quantities. Research and sample quantities and hygroscopic, oxidizing or other air sensitive materials may be packaged under argon or vacuum. Solutions are packaged in polypropylene, plastic or glass jars up to palletized 941 gallon liquid totes Special package is available on request. HANG JIs’ is carefully handled to minimize damage during storage and transportation and to preserve the quality of our products in their original condition